    題名: A newly developed Fe-doped calcium sulfide nanoparticles with magnetic property for cancer hyperthermia
    作者: Wu, SYH;Tseng, CL;Lin, FH
    貢獻者: Division of Medical Engineering Research
    摘要: In this study, a magnetic iron-doped calcium sulfide (Fe-CaS) nanoparticle was newly developed and studied for the purpose of hyperthermia due to its promising magnetic property, adequate biodegradation rate, and relatively good biocompatibility. Fe-CaS nanoparticles were synthesized by a wet chemical co-precipitation process with heat treatment in a N2 atmosphere, and were subsequently cooled in N2 and exposed to air at a low temperature. The crystal structure of the Fe-CaS nanoparticles was similar to that of the CaS, which was identified by an X-ray diffractometer (XRD). The particle size was less than 40 nm based on a Debye-Scherrer equation and transmission electron microscope (TEM) examination. Magnetic properties obtained from the SQUID magnetometer demonstrated that the synthesized CaS was a diamagnetic property. Once the Fe ions were doped, the synthesized Fe-CaS converted into paramagnetism which showed no hysteresis loop. Having been heated above 600 ?C in N2, the Fe-CaS showed a promising magnetic property to produce enough energy to increase the temperature for hyperthermia. 10 mg/ml of the Fe-CaS was able to generate heat to elevate the media temperature over 42.5 ?C within 6 min. The area of the hysteresis loop increased with the increasing of the treated temperature, especially at 800 ?C for 1 h. This is because more Fe ions replaced Ca ions in the lattice at the higher heat treatment temperature. The heat production was also increasing with the increasing of heat treatment temperature, which resulted in an adequate specific absorption ratio (SAR) value, which was found to be 45.47 W/g at 37 ?C under an alternative magnetic field of f = 750 KHz, H = 10 Oe. The in vitro biocompatibility test of the synthesized Fe-CaS nanoparticles examined by the LDH assay showed no cytotoxicity to 3T3 fibroblast. The result of in vitro cell hyperthermia shows that under magnetic field the Fe-CaS nanoparticles were able to generate heat and kill the CT-26 cancer cells significantly. We believe that the developed Fe-CaS nanoparticles have great potential as thermo-seeds for cancer hyperthermia in the near future.
    日期: 2010-05
    關聯: Journal of Nanoparticle Research. 2010 May;12(4):1173-1185.
    Link to: http://dx.doi.org/10.1007/s11051-009-9734-7
    JIF/Ranking 2023: http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=NHRI&SrcApp=NHRI_IR&KeyISSN=1388-0764&DestApp=IC2JCR
    Cited Times(WOS): https://www.webofscience.com/wos/woscc/full-record/WOS:000276883600011
    Cited Times(Scopus): http://www.scopus.com/inward/record.url?partnerID=HzOxMe3b&scp=77955088428
    顯示於類別:[林峯輝] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    SCP68449104273.pdf443KbAdobe PDF449檢視/開啟


    在NHRI中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋